| Hot mounting resins | ||
| To respond to all metallographic control and research situations, LAM PLAN developed and tested a range of hot mounting resins which allow obtaining perfectly adapted mountings regardless. |
| Acrylic hot mounting resins | |||
| Acrylic resin 616 | |||
| The acrylic resin 616 is perfectly transparent and adapted to most materials. Mainly used to view the evolution of the grinding of the sample. | |||
 |
Characteristics | Qty/kg | Ref. |
| Transparent acrylic powder Visualising the sample during and after the polishing All materials |
2,510 | 06 00616 2006 00616 10 | |
| Acrylic resin 616.2 | |||
| Perfectly transparent with no cotton effect, the acrylic resin 616.2 is resistant to alcohol, and therefore ideal for work with alcohol-based polishing products or requiring a cleaning phase with ethanol, isopropyl alcohol or other. | |||
 |
Characteristics | Qty/kg | Ref. |
| Transparent acrylic powder Visualising the sample during and after the polishing Water resistant |
2,510 | 06 06162 2006 06162 10 | |
กกก
| Guidance |
 * Depending of the machines’ characteristics |
| Diagnosis and guidance for LAM PLAN resin |
| Before to begin any mounting process, the grease needs to be removed from the samples in order for the resin to adhere to the contours of the parts. Check if any burrs were committed in the cutting process. If necessary, deburr the sample’s edges with an abrasive paper
|
| Copper hot mounting resin | |||
| Conductive mounting resin for examinations with SEM or electrolytic etching device. A pure copper based resin of very homogeneous consistency, the conductibility of your mountings is optimised. The use of ultra-pure materials eliminates the risk of an analysis error. | |||
| Copper resin 604.3 | |||
 |
Characteristics | Qty/kg | Ref. |
| Resinoid copper powder For electrolytic polishing |
2 | 06 00604 30 | |
กกก
| Guidance |
| * Depending of the machines’ characteristics |
| Diagnosis and guidance for LAM PLAN resin |
| Before to begin any mounting process, the grease needs to be removed from the samples in order for the resin to adhere to the contours of the parts. Check if any burrs were committed in the cutting process. If necessary, deburr the sample’s edges with an abrasive paper
|
| Epoxy hot mounting resins | |||
| The black epoxy mounting resin is filled with glass fibres with high mineral loads. It is ideal for mountings intended for edge examinations of hard to extra hard materials thanks to its resistance to abrasion, important hardness and absence of shrinkage | |||
| Epoxy resin 633 | |||
 |
Characteristics | Qty/kg | Ref. |
| Black epoxy powder, loaded with glass fibres Edges examinations Extra hardness – No shrinkage |
2,5
10 |
06 00633 20
06 00633 10 |
|
| Epoxy resin 634 | |||
| The 634 is a fine powder epoxy resin, used for examination of edged samples. |
|||
 |
Characteristics | Qty/kg | Ref. |
| Black epoxy powder, fine grains Edge examinations on complex samples High hardness – No shrinkage |
2,5 | 06 00634 20 | |
กกก
| Guidance |
| * Depending of the machines’ characteristics |
| Diagnosis and guidance for LAM PLAN resin |
| Before to begin any mounting process, the grease needs to be removed from the samples in order for the resin to adhere to the contours of the parts. Check if any burrs were committed in the cutting process. If necessary, deburr the sample’s edges with an abrasive paper
|
| Graphite hot mounting resin | |||
| Graphite resin 617 | |||
| Conductive phenolic mounting resin loaded with graphite (without copper and without metals or alloys) for SEM and TEM examinations. | |||
 |
Characteristics | Qty/kg | Ref. |
| Conductive black phenolic powder (graphite) For SEM examination |
1,5 | 06 00617 00 | |
กกก
| Guidance |
| * Depending of the machines’ characteristics |
| Diagnosis and guidance for LAM PLAN resin |
| Before to begin any mounting process, the grease needs to be removed from the samples in order for the resin to adhere to the contours of the parts. Check if any burrs were committed in the cutting process. If necessary, deburr the sample’s edges with an abrasive paper
|
| PHENOFREE hot mounting resins – PHENOL free | |||
| New phenol-free and formaldehyde-free thermosetting mounting resin In line with its ecological commitment, LAM PLAN proposes on the market the first effective alternative to phenol metallographic mounting resins which are liable to release phenol (and/or formaldehyde) during baking.The PHENOFREE mounting is intended for the technical mounting of all types of materials for material examinations or edge examinations. It smartly replaces the traditional phenol mounting resins with the same hardness and less shrinkage than a phenol mounting resins.The range of PHENOFREE resins includes 3 coloured resins (grey, white and red) to make the identification of your metallographic samples easier. They are particularly adapted for the polishing of hard materials. The white Phenofree resin may prove to be in some cases a good alternative to the use of epoxy resins. |
|||
| PHENOFREE 1 | |||
 |
Characteristics | Qty/kg | Ref. |
| Grey composite powder Polyvalent, hard |
1,5 10 25 |
06 PF010 20 06 PF010 10 06 PF010 50 |
|
| PHENOFREE 2 | |||
 |
Characteristics | Qty/kg | Ref. |
| Red composite powder Polyvalent, very hard |
2,5 10 25 |
06 PF020 20 06 PF020 10 06 PF020 50 |
|
| PHENOFREE 3 | |||
 |
Characteristics | Qty/kg | Ref. |
| Poudre composite blanche Polyvalente, extra dure |
2,5 10 25 |
06 PF030 20 06 PF030 10 06 PF030 50 |
|
กกก
| Guidance |
| * Depending of the machines’ characteristics |
| Diagnosis and guidance for LAM PLAN resin |
| Before to begin any mounting process, the grease needs to be removed from the samples in order for the resin to adhere to the contours of the parts. Check if any burrs were committed in the cutting process. If necessary, deburr the sample’s edges with an abrasive paper
|